Mastertac Technical Information

View   
23.11.2016 ENG 832
SELF-ADHESIVESHEETS
FACEPP SOLID WHITE M TC
PPCHY (sales code)
ProductA white, glossy, biaxially oriented, solid, top-coated polypropylene film.
UseMultipurpose white film for rigid containers, where good water, chemical and oil resistance is needed. High cohesive strength provides resistance against delamination and stretching, required in repositionable and open-closure applications.
Typical technical values
Substance
57 g/m² ISO 2286-1/2/3
Caliper
59 µm ISO 2286-1/2/3
Tensile strength MD
150 MPa ISO 527-1/3
Tensile strength CD
270 MPa ISO 527-1/3
Gloss
80 % DIN 67530/1 60º
PrintabilitySuitable for flexography, screen and offset printing methods. Special inks designed for non-absorbent materials should be used. Suitable also for printing on Xeikon digital label presses. Thermal transfer possible with selected wax-resin and resin ribbons.
AdvantagesVery high gloss. High stiffness and dimensional stability. High tensile and tear strength. Good register control.
Disclaimer
The performance of the product should always be tested in the actual application conditions. Our recommendations are based on our most current knowledge and experience. As our products are used in conditions beyond our control, we cannot assume any liability for damage caused through their use. Users of our products are solely responsible that the product is suitable for its intended application, and have determined such at their sole discretion. Users must comply with any applicable legislation and/or testing requirements for the finished article, and are responsible for bringing their products to market. This publication does not constitute any warranty, express or implied, and is intended only for the recipient and cannot therefore be transferred to any third party. We cannot assume any liability for the use of our products in conjunction with other materials. All our products are sold subject to UPM Raflatac’s general sales conditions, and you should ensure that any existing laws are observed. This publication replaces all previous versions. All information is subject to change without notice.

   Download printable version: